Alloy A-286 is designed for applications requiring high strength and good corrosion resistance at temperatures up to 1300 °F(704 °C). This alloy offers high ductility in notched sections. In fact, the notched rupture strength of alloy A-286 is superior to many other commercial alloys with comparable high temperature properties. An advantage of this alloy is that it can be precipitation hardened and strengthened by heat treatments. This makes possible a high degree of uniformity in developing maximum strength, which can be duplicated application after application.
| ALLOY | SIZE | WEIGHT |
|---|---|---|
| CURRENT BAR INVENTORY | ||
| A286 BAR COLD REDUCED AMS 5726 200KSI | 0.188 DIA X 160-162RL 4.7752MM DIA | 1588 LBS 720 KG |
| A286 BAR COLD REDUCED AMS 5726 200KSI | 0.260 DIA X 161RL 6.604MM DIA | 1782 LBS 808 KG |
| A286 BAR COLD REDUCED AMS 5726 200KSI | 0.322 DIA X 162RL + 129 8.1788MM DIA | 1967 LBS 892 KG |
| A286 BAR COLD REDUCED AMS 5726 200KSI | 0.385 DIA X 161RL 9.779MM DIA | 1517 LBS 688 KG |
| A286 BAR COLD REDUCED AMS 5726 200KSI | 0.510 DIA X 161"RL 12.954MM DIA | 1889 LBS 857 KG |
| A286 BAR COLD REDUCED AMS 5726 200KSI | 0.635 DIA X 132-156RL 16.129MM DIA | 1324 LBS 601 KG |
| A286 BAR COLD REDUCED AMS 5726 200KSI | 0.760 DIA X 140-164RL 19.304MM DIA | 1363 LBS 618 KG |
| A286 BAR COLD REDUCED AMS 5726 200KSI | 1.010 DIA X 136-161RL 25.654MM DIA | 1095 LBS 497 KG |
| A286 BAR COLD REDUCED AMS 5726 200KSI | 1.260 DIA X 159-168RL+142 32.004MM DIA | 870 LBS 395 KG |
| A286 BAR COLD REDUCED AMS 5726 200KSI - DUE DATE: 07-20-27 | 1.260 DIA X 160" RL 32.004MM DIA | 1487 LBS 674 KG |